Pengaruh Variasi Temperatur Heat Treatment Terhadap Kekerasan Pada Sprocket Honda Tiger 200cc
Keywords:
Sprocket, Heattreatment, Kekerasan, RockwellAbstract
This study aims to determine the effect of temperature variation Heat treatment sprocket honda tiger 200cc with temperature variations of 750⁰c, 800⁰c, 850⁰c and 900⁰c. Using the Rockwell hardness test. From the test results, the highest hardness value at 900⁰c was 61.39 HRA for the ORI sprocket while the KW sprocket at 800⁰c was 45.43 HRA, the lowest hardness value at 800⁰c was 48.05 HRA for the ORI sprocket and while the KW sprocket at 750⁰c was 40.02 HRA. From the results obtained, it can be concluded that the Rockwell hardness test on the Honda Tiger 200cc sprocket with the heat treatment method can affect the mechanical properties of the metal alloy.
Keywords: Sprocket, Heattreatment, Hardness, Rockwell.
Penelitian ini bertujuan untuk mengetahui pengaruh variasi temeperatur Heat treatment sprocket honda tiger 200cc dengan variasi temperature 750⁰c,800⁰c,850⁰c dan 900⁰c. Menggunakan uji kekerasan Rockwell. Dari hasil pengujian didapatkan nilai kekerasan tertinggi pada suhu 900⁰c adalah 61.39 HRA untuk sprocket ORI sedangkan sprocket KW pada suhu 800⁰c adalah 45.43 HRA, nilai kekerasan terendah terendah pada suhu 800⁰c adalah 48.05 HRA untuk sprocket ORI dan sedangkan sprocket KW pada suhu 750⁰c adalah 40.02 HRA. Dari hasil yang telah didapatkan dapat disimpulkan bahwa perlakuan uji kekerasan Rockwell pada sprocket honda tiger 200cc dengan metode Heat treatment dapat mempengaruhi sifat mekanis paduan logam tersebut.
Kata kunci: Sprocket, Heattreatment, Kekerasan, Rockwell.
Downloads
References
D. Kurnia, B. Widodo, M. Anhar, A. Halim, P. Mesin, and P. N. Ketapang, “JOURNAL OF APPLIED MECHANICAL ENGINEERING AND RENEWABLE ENERGY ( JAMERE ) Uji Kekerasan Bahan Gear Sprocket Dengan Campuran Timah ( Sn ),” J. Appl. Mech. Eng. Renew. ENERGY ( JAMERE ) Uji Kekerasan Bahan Gear Sprocket Dengan Campuran Timah ( Sn ), vol. 1, no. 1, pp. 16–19, 2021.
Y. Rizal and Ismardi, “Pengaruh perlakuan panas terhadap sifat kekerasan (hardness) pada roda gigi tarik sepeda motor honda,” J. Fak. Tek. Univ. Pasir Pengaraian, pp. 139–144, 2015.
N. H. Sari, “Perlakuan Panas Pada Baja Karbon: Efek Media Pendinginan Terhadap Sifat Mekanik Dan Struktur Mikro,” J. Tek. Mesin, vol. 6, no. 4, p. 263, 2017, doi: 10.22441/jtm.v6i4.2091.
T. C. Wahyudi, E. Nugroho, E. Budiyanto, and M. F. Maktum, “Kaji Eksperimen Pengaruh Variasi Temperatur Pemanasan dan Media Pendingin pada Proses Quenching terhadap Perubahan Kekerasan Sprocket Gear Sepeda Motor Non Original Experimental Study of the Effect of Variations in Heating and Cooling Media Temperatures i,” vol. 06, 2021.
P. Carburizing, “Analisa Pengaruh Pack Carburizing Menggunakan Arang Mlanding … ( Mas’ad dkk. ),” pp. 40–45, 2011.
N. Ilyas et al., “PENGARUH VARIASI SILIKON KARBIDA ( SiC ) PADA PADUAN ALUMINIUM ( Al ) DALAM PEMBUATAN,” vol. 1, no. 1, 2016.
R. Rifnaldi and Mulianti, “Pengaruh Perlakuan Panas Hardening dan Tempering Terhadap Kekerasan (Hardness) Baja AISI 1045,” Ranah Res. J. Multidicsiplinary Res. Dev., vol. 1, no. 4, pp. 950–959, 2019.
V. Bhaskara Sardi, S. Jokosisworo, and H. Yudo, “JURNAL TEKNIK PERKAPALAN Pengaruh Normalizing dengan Variasi Waktu Penahanan Panas (Holding Time) Baja ST 46 terhadap Uji Kekerasan, Uji Tarik, dan Uji Mikrografi,” J. Tek. Perkapalan, vol. 6, no. 1, p. 142, 2018, [Online]. Available: http://ejournal3.undip.ac.id/index.php/naval
Z. Fatoni, “Pengaruh Perlakuan Panas Terhadap Sifat Kekerasan Baja Paduan Rendah Untuk Bahan Pisau Penyayat Batang Karet,” J. Desiminasi Teknol., vol. 4, no. 1, pp. 56–63, 2016.
Downloads
Published
Issue
Section
License
Copyright (c) 2023 Delpi Ero Tirta Pratama Delpi, Dini Kurniawati, Mulyono
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.