Comparison of Corrosion Rate on Paint Coated and Uncoated SS400 Steel

Authors

  • Eko Hariyadi University of Muhammadiyah Malang
  • Mohammad Jufri University of Muhammadiyah Malang
  • Hasanuddin Hasanuddin University of Muhammadiyah Malang

DOI:

https://doi.org/10.22219/jemmme.v2i1.4904

Abstract

To prevent corrosion in metal, especially carbon steel, always need efforts which considered expensive one. But, compared with costs and losts when the corrosion attack is not properly managed then the cost of efforts is much lower. The most popular method in preventing corrosion attack is by coating of metal which also has decorative objective. In this research, four coating materials were applied to the surface of low carbon steel strips (SS400) and as control uncoated SS400 steel strips were also employed. The steel strips then were dipped into electrolite solution consisted of 30% of consentration of H2SO4, and NaCl soluted in river water for 15 (fifteen) days. After the presetted time was elapsed, the steel strips then examined for lost of mass. It was found that the highest lost of mass was for unpolished uncoated one dipped in H2SO4 with corrosion rate of 4,566.06 mpy. The lowest lost was for paint coated one dipped in NaCl-river water solution with corroion rate of 0.64 mpy.

Downloads

Download data is not yet available.

References

Amsori M Das, Studi Dampak Korosi Terhadap Internal Baja, Jurnal Ilmiah Ilmu Batanghari Jambi, 2012, Vol.12 No.2.

Tezar Prima Nurhamzah, Studi Laju Korosi Pada Sampel Pipa Baja Api 5L X-52 Dengan Pengaruh Variasi Kecepatan Putaran dan Gas CO2Pada ph6 dalam Larutan NaCl 3.5 %, Skripsi, Depok, Fakultas Teknik,Jurusan Teknik Metalurgi dan Material, 2011.

Syahbuddin dan Abdul Rahman, Pertumbuhan Lapisan Intermetalik Fe-Zn Pada Permukaan Sambungan Las Baja Struktur SS400 Selama Galvanis Pada 460®c ,Jurnal Desain Dan Kontruksi, 2003, Volume 2 No.1.

Yudha Kurniawan Afandi, Analisa Laju Korosi Pada Pelat Baja Karbon Dengan Ketebalan Coating, Jurnal Teknik ITS, 2015, Vol.4.No.1(2015) ISSN 2337-3539 (2301-9271 Printed)

M Fajar Sidiq, Analisa Korosi dan Pengendaliannya, Jurnal Foundry, 2013, Vol,3 No.1 April 2013 ISSN :2087-2259

Athanasius P. Bayuseno, Analisa Laju Korosi Pada Baja untuk Material Kapal Dengan dan Tanpa Perlindungan Cat, 2009, Jurnal Vol.11 No,3,Semarang.

Kenneth R Trethewey, dan John Chamberlin, Korosi Untuk Mahasiswa dan Rekayasawan, Terjemahan Alex Tri Kantjono Widodo , Jakarta, PT. Gramedia Pustaka Utama, 1991.

Bagus Sanjaya Putra, Perbandingan Laju Korosi Pada Baja EMS 45 Berpelapis dan Tanpa Pelapis Terhadap Konsentrasi Asam Sulfat, Skripsi, Malang, Teknik Mesin,Fakultas Teknik, UMM, 2013.

Downloads

Published

2017-11-09

How to Cite

Hariyadi, E., Jufri, M., & Hasanuddin, H. (2017). Comparison of Corrosion Rate on Paint Coated and Uncoated SS400 Steel. Journal of Energy, Mechanical, Material, and Manufacturing Engineering, 2(1), 49–54. https://doi.org/10.22219/jemmme.v2i1.4904

Issue

Section

Articles