Pembuatan Beton Ringan Dari Aggregat Buatan Berbahan Plastik
Main Article Content
Abstract
Pembuatan Beton Ringan Dari Aggregat Buatan Berbahan Plastik
Making Lightweight Aggregate Concrete From Artificial Plastic
Erwin Rommel
Jurusan Teknik Sipil Fakultas Teknik Universitas Muhammadiyah MalangJalan Raya Tlogomas 246 Malang 65144email : erwin67pro@yahoo.com
ABSTRACT
Plastic is the type of waste non-biodegradable, although in the long term. It is therefore necessary to use plastic waste soon This research begins with the manufacture of aggregate through the choppe process, heating and molding of High Density Polyethylene plastic waste into piece of aggregate size of 20 mm. Then test the characteristics of aggregate, mix design and provide concrete with heat treatment at each temperature 30, 45, 60, 75, 90 and 1100 C. The test of results obtained plastic aggregate specific gravity 1.15; bulk density 1378 kg/m3; aggregate abrasion 29.64% explained that the aggregate can be used as the lightweight concrete. Lightweight concrete made with a mix design ratio of cement: sand: aggregate of plastic 1:2:1,5 and fas 0.35 obtained maximum compressive strength of 13.16 MPa so that the concrete in the category for the use of lightweight structures such as wall panels, concrete sills , cladding. Appropriate use of lightweight concrete for structures that are protected because of the high temperatures can reduce the strength of concrete. High absorption rate of 8.043% and a porosity of 10.7% suggested the use of lightweight concrete in areas that have low levels of humidity.
Keywords: Lightweight concrete, plastic artificial aggregate, compressive strength
ABSTRAK
Plastik adalah jenis sampah non-biodegradable, meskipun dalam jangka panjang. Oleh karena itu perlu menggunakan sampah plastik segera Penelitian ini dimulai dengan pembuatan agregat melalui proses Choppe, pemanasan dan molding dari High Density Polyethylene sampah plastik menjadi bagian dari ukuran agregat dari 20 mm. Kemudian menguji karakteristik agregat, campuran desain dan menyediakan beton dengan perlakuan panas pada setiap suhu 30, 45, 60, 75, 90 dan 1100 C. Pengujian hasil yang diperoleh plastik berat jenis agregat 1,15; bulk density 1378 kg / m3; abrasi agregat 29,64% menjelaskan bahwa agregat dapat digunakan sebagai beton ringan. Beton ringan dibuat dengan rasio desain campuran semen: pasir: agregat plastik 1: 2: 1,5 dan fas 0,35 diperoleh kuat tekan maksimum 13,16 MPa sehingga beton dalam kategori penggunaan struktur ringan seperti panel dinding , kusen beton, cladding. Penggunaan yang tepat beton ringan untuk struktur yang dilindungi karena suhu tinggi dapat mengurangi kekuatan beton. Tingkat penyerapan tinggi 8,043% dan porositas 10,7% menyarankan penggunaan beton ringan di daerah yang memiliki tingkat kelembaban yang rendah.
Kunci-kata: Beton ringan, plastik agregat buatan, kuat tekan
Making Lightweight Aggregate Concrete From Artificial Plastic
Erwin Rommel
Jurusan Teknik Sipil Fakultas Teknik Universitas Muhammadiyah MalangJalan Raya Tlogomas 246 Malang 65144email : erwin67pro@yahoo.com
ABSTRACT
Plastic is the type of waste non-biodegradable, although in the long term. It is therefore necessary to use plastic waste soon This research begins with the manufacture of aggregate through the choppe process, heating and molding of High Density Polyethylene plastic waste into piece of aggregate size of 20 mm. Then test the characteristics of aggregate, mix design and provide concrete with heat treatment at each temperature 30, 45, 60, 75, 90 and 1100 C. The test of results obtained plastic aggregate specific gravity 1.15; bulk density 1378 kg/m3; aggregate abrasion 29.64% explained that the aggregate can be used as the lightweight concrete. Lightweight concrete made with a mix design ratio of cement: sand: aggregate of plastic 1:2:1,5 and fas 0.35 obtained maximum compressive strength of 13.16 MPa so that the concrete in the category for the use of lightweight structures such as wall panels, concrete sills , cladding. Appropriate use of lightweight concrete for structures that are protected because of the high temperatures can reduce the strength of concrete. High absorption rate of 8.043% and a porosity of 10.7% suggested the use of lightweight concrete in areas that have low levels of humidity.
Keywords: Lightweight concrete, plastic artificial aggregate, compressive strength
ABSTRAK
Plastik adalah jenis sampah non-biodegradable, meskipun dalam jangka panjang. Oleh karena itu perlu menggunakan sampah plastik segera Penelitian ini dimulai dengan pembuatan agregat melalui proses Choppe, pemanasan dan molding dari High Density Polyethylene sampah plastik menjadi bagian dari ukuran agregat dari 20 mm. Kemudian menguji karakteristik agregat, campuran desain dan menyediakan beton dengan perlakuan panas pada setiap suhu 30, 45, 60, 75, 90 dan 1100 C. Pengujian hasil yang diperoleh plastik berat jenis agregat 1,15; bulk density 1378 kg / m3; abrasi agregat 29,64% menjelaskan bahwa agregat dapat digunakan sebagai beton ringan. Beton ringan dibuat dengan rasio desain campuran semen: pasir: agregat plastik 1: 2: 1,5 dan fas 0,35 diperoleh kuat tekan maksimum 13,16 MPa sehingga beton dalam kategori penggunaan struktur ringan seperti panel dinding , kusen beton, cladding. Penggunaan yang tepat beton ringan untuk struktur yang dilindungi karena suhu tinggi dapat mengurangi kekuatan beton. Tingkat penyerapan tinggi 8,043% dan porositas 10,7% menyarankan penggunaan beton ringan di daerah yang memiliki tingkat kelembaban yang rendah.
Kunci-kata: Beton ringan, plastik agregat buatan, kuat tekan